1-K PU foam pro B3
1C assembly foam PUR Asia Economic
ASMBYFM-1C-MAN-B3-750ML
Register now and access more than 2,000 products
- Pre-foaming
- Good insulation characteristics
- High thermal and acoustical insulation
- High adhesion to most building materials
- Excellent stability
- Filling joints cracks and gaps in insulating panels and sheets
- Excellently suitable as foam for sealing and connecting precast concrete well shaft rings
- CFC-free & harmless to the ozone layer
This information is only intended as a recommendation based on our own experience. The use should always perform his own preliminary testing.
Datasheets(X)
- Installing, fixing and insulating of door and window frames
- Filling and sealing of gaps, joint, openings and cavities
- Connecting of insulation materials and roof construction
- Installing, fixing and insulating of door and window frames
- Clean with a cleaning agent, to keep the substrate surfaces completely clean.
- Shake the can for over 1 mins.
- Fill vertical gaps from the bottom up (pay attention to foam expansion).
- Turn off the flow adjustment screw clockwise direction when finishing.
- Before curing, foam can be moved and cleaned with PU cleaner either with the gun or with adapter. Cleaning of the screw adapter with cleaner is recommended.
Chemical basis | Polyurethane |
Colour | Light yellow |
Density | 20 kg/m³ |
Density conditions | at 23°C, 50% relative humidity |
Moulded density | 1 g/cm³ |
Cell structure | Medium - fine |
Tack-free after | 12 min |
Conditions for being tack-free | at 20°C and 65% humidity |
Can be cut after | 50 min |
Conditions for ability to cut | at 20°C and 65% relative humidity at 30-mm adhesive line |
Full resilience | 2 min |
Min. processing temperature | 5 °C |
Min. ambient processing temperature | 5 °C |
Min. surface processing temperature | 0 °C |
Max. processing temperature for can | 35 °C |
Min./max. temperature resistance | -20 to 90 °C |
Max. short-term temperature resistance | 80 °C |
Heat conductance λ | 0.046 W/(m*K) |
Flexural strength | 85 kPa |
Conditions for flexural strength | after 28 days, 23°C and 50% relative humidity |
Shear strength | 114 kPa |
Conditions for shear strength | in accordance with DIN 53427 |
Compressive strength | 3 N/cm |
Compressive strength conditions | after 28 days, 23°C and 50% relative humidity |
Breaking elongation | 60 % |
Breaking elongation conditions | in accordance with ASTM D-412 |
Yield (volume) approx. | 38 l |
Conditions for yield | at 23°C and 50% humidity, in released form |
Contents | 750 ml |
Container | Aerosol can |
Weight of content | 725 g |
Building material class | B3 - Of high flammability |
Building material class conditions | in accordance with DIN 4102 |
Shelf life from production | 12 Month |
Conditions to maintain shelf life from production | at 5°C to 25°C |
Last viewed
Adhesive lubricant HHS® 1000
Radiator cleaner
Sledgehammer German design in accordance with DIN 1042
Mudguard pincers
1" slider bar With pin detent
Twist Drill bits HSS ASME B94.11M TYPE RN
Multigrade compressor oil Pro
1/2 inch socket wrench insert metric, hexagon, short
Hook-&-Loop Foam Pad Flexible Rotary Polisher
Electrician's scissors stainless, hardened, matte