Corrosion protection coating Zinc 300

Name: Corrosion protection coating Zinc 300
Brand: Würth
SKU: 0892200

Corrosion protection lacquer Zinc 300
CORRPROTLAC-ZINC300-SPREADABLE-500ML

Art.-no. 0892200

EAN 4011231829311

All versions

Prices for customers after login

Corrosion protection coating Zinc 300

Art.-no. 0892200

Prices for customers after login

Quantity

x 1 pcs

Exclusively for trade customers

Login/Register
Call customer service: +94 112 894930

Provides permanent protection against corrosion

Excellent corrosion protection

Quick drying

Appearance: Hot-dip zinc-plated

Can be painted over

PVC-based paints, acrylate (solvent-based or aqueous) are suitable.

Do not paint with alkyd resins (synthetic resin paints) in combination with hot-dip zinc-plated surfaces!

The usage instructions are recommendations based on the tests we have conducted and on our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. If our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee the consistent quality of our products. We reserve the right to make technical changes and further develop products.

Product information

Würth Catalogue

Datasheets(X)

Certificates/ Documents

Application area

Steel construction, shipbuilding, forging, fitter's shops and vehicle construction.

Zinc 300 is suitable for touching up damaged spots on zinc-plated surfaces and welding seams.

Not suitable as zinc-dust primer for heavy-duty corrosion protection.

Instructions

The surface must be clean, dry and free from dust and grease. The layer thickness of the touch-up film should equal 1.5 times that of hot-dip zinc-plating. In addition, the touch-up coating should overlap the hot-dip zinc-plating by at least 1 cm. Consumption: approx. 250-350 g/m per coat.

Contents	500 ml
Weight of content	1045 g
Chemical basis	Fixed metallic zinc dust
Colour	Silver coloured
Conditions for drying time	at 20°C
Min./max. processing temperature	-25 to 40 °C
Max. through drying	3 d
Min. through drying	2 d
Drying time	15 min
Zinc content in the paint	65 %
Zinc content in the dry film	91 %
Purity rating zinc	99 %
Density	2.09 g/cm³
Density conditions	at 20°C
Max. temperature resistance	300 °C
Min. grip strength	45 min
Shelf life from production	12 Month

Suitable glove:

Product

Description

Nitrile chemical protective glove With cotton velour finish inside

Description:

Permeation level: 5

Nitrile chemical protective glove Long, heavy-duty design

Description:

Permeation level: 6

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time

Permeation level

< 10 min

≥ 10 min

≥ 30 min

≥ 60 min

≥ 120 min

≥ 240 min

≥ 480 min

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.