Structural adhesive, Bond+Seal
Prices for customers after login
Register now and access more than 2,000 products
For universal use
Outstanding adhesive strength on a wide range of materials and surfaces
Approved for use with foodstuffs (ISEGA certificate)
Long skin formation time
Can be sanded and painted over
Following skin formation, it can be mechanically machined and painted over without surface activation (perform preliminary tests to check paint compatibility).
Prevents metal corrosion
Can be used where food is processed or stored, e.g. for bonding wall and floor areas in food processing companies.
Clearance certificate no.: 41958 U 16
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.
The application surfaces must be clean, dry and free of grease. For pre-treatment, please refer to the optimisation table in the technical data sheet.
Cut off the thread cap, screw on the nozzle and cut it to the required width. Apply the adhesive using a suitable application gun. A minimum adhesive layer thickness of 3 mm is recommended to harness the benefits of thick-coat bonding.
For more information, please refer to the technical data sheet.
Single component polyurethane
Min./max. skin-formation time
Min./max. skin-formation time /conditions
45-60 min / at 23°C and 50% relative humidity
Full curing speed/conditions
3 mm/d / 23°C and 50% relative humidity, moisture curing
1.25 g/cm³ / prior to hardening, DIN 53479
Min. tensile strength
Min. combined tension and shear resistance
Conditions for tensile strength
in accordance with DIN 53504
Min. longitudinal resistance to tearing
Conditions for resistance to tearing
in accordance with DIN 53515
Elongation at break/conditions
500 % / in accordance with DIN 53504
Min./max. processing temperature
5 to 35 °C
Min./max. temperature resistance
-40 to 90 °C
Max. short-term temperature resistance
Min. flashing point
Glass transition temperature/conditions
-45 °C / in accordance with DIN 53445
Max. change in volume
Shelf life from production/conditions
12 Month / at 10°C to 25°C